In the current research, we have utilized sol-gel electrophoresis technique to grow PbTiO3 nanotube arrays in porous anodic alumina template channels. By using this method high quality and more condense nanotubes are obtained compared with other usual sol-gel methods. Also, the effect of the anodizing parameters on the diameter of the template pores, and effect of electrophoresis voltage on wall thickness were investigated.

In this paper, we explore the interfacial effects appearing in highly strained La0.7Ca0.3MnO3 (LCMO) ultra-thin films (10-12nm) grown on BaTiO3 (BTO) ferroelectric substrates. The strong tendency to phase separation of this optimally doped manganite contributes to the exotic phenomena observed in magnetism and transport experiments: the so-called Matteucci magnetic loops, magnetic granularity and a second metal insulator transition are observed between 50K and the LCMO Curie temperature, 180K. All these properties define the multiferroic character of these heterostructures, which in LCMO//BTO system is strongly linked to magnetoelastic coupling.

Pentacene-based ferroelectric gate transistors with croconic acid (CrA) thin film was fabricated for the first time. The memory window (MW) of 1.9 V was obtained from the capacitance-voltage (C-V) characteristics of Al/CrA(50 nm)/SiO2/Si(100) metal-ferroelectric-insulator-semiconductor (MFIS) diode, where the deposition temperature of CrA was room temperature (RT). Butterfly type C-V characteristics was observed for Al/CrA(50 nm)/Al/SiO2/ Si(100) metal-ferroelectric-metal (MFM) diode. Furthermore, a pentacene-based p-type organic field-effect transistor (OFET) with CrA gate insulator was fabricated, and clockwise hysteresis loop was observed in ID-VG characteristic, which is attributed to the ferroelectric properties of CrA gate insulator.