Microstructure and mechanical properties of fiber laser welded joints of ultrahigh-strength steel 22MnB5 and dual-phase steels

Published online by Cambridge University Press:  08 October 2014

Jin Jia*
Affiliation:
College of Materials Engineering, Shanghai University of Engineering Science, Shanghai 201620, China
Shang-Lei Yang
Affiliation:
College of Materials Engineering, Shanghai University of Engineering Science, Shanghai 201620, China; and Shanghai Research and Development Center for Key Technologies of Intelligent Equipments of Ultra-intense Laser Processing (Shanghai University of Engineering Science), Shanghai 201620, China
Wei-Yuan Ni
Affiliation:
College of Materials Engineering, Shanghai University of Engineering Science, Shanghai 201620, China
Jian-Ying Bai
Affiliation:
College of Materials Engineering, Shanghai University of Engineering Science, Shanghai 201620, China
*
a)Address all correspondence to this author. e-mail: yzjiajin@126.com
Get access

Abstract

This study was to analyze the microstructure, microhardness, tensile and fatigue performance of the welded joints performed by a fiber laser on 22MnB5 and dual-phase steels (DP590, DP980) in similar and dissimilar combinations. The result shows that the weld zone (WZ) basically consisted of lath martensite. The HAZ in these steels can be divided into 3 parts: quenched, incomplete quenched, and tempered region. The WZ had the highest hardness, and a soft zone existed in the HAZ of all steels. Inside the WZ of the dissimilar welded joints, two hardness subregions were observed due to the difference in the alloying elements of these steels. Tensile specimens of the 22MnB5–22MnB5 and 22MnB5–DP980 welded joints were all broken in HAZ, while the 22MnB5–DP590 welded joints failed in the DP590 base metal (BM). The BM had a higher fatigue life than the welded joints, and the fatigue failure of the 22MnB5 similar and 22MnB5–DP980 dissimilar welded joints respectively occurred in the HAZ and DP980 BM. The fatigue fracture contained 3 parts: crack initiation, crack propagation, and the final fast fracture region.

Type
Articles
Copyright
Copyright © Materials Research Society 2014 

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

REFERENCES

Cao, X. and Jahazi, M.: Effect of welding speed on butt joint quality of Ti-6Al-4V alloy welded using a high-power Nd: YAG laser. Opt. Laser Eng. 47, 1231 (2009).Google Scholar
Park, Y.W., Park, H., Rhee, S., and Kang, M.: Real time estimation of CO2 laser weld quality for automotive industry. Opt. Laser Technol. 34, 136 (2002).CrossRefGoogle Scholar
Sokolov, M., Salminen, A., Kuznetsov, M., and Tsibulskiy, I.: Laser welding and weld hardness analysis of thick section S355 structural steel. Mater. Des. 32, 5127, (2011).Google Scholar
Karbasian, H. and Tekkaya, A.E.: A review on hot stamping. J. Mater. Process. Technol. 210, 2103 (2010).Google Scholar
Kim, C.H., Choi, J.K., Kang, M.J., and Park, Y.D.: A study on the CO2 laser welding characteristics of high strength steel up to 1500MPa for automotive application. J. Achiev. Mater. Manuf. Eng. 39, 79 (2010).Google Scholar
Hyunwoo, S., Dennis, F., Hartmut, H., Roland, G., and Mirko, S.: An investigation of the blanking process of the quenchable boron alloyed steel 22MnB5 before and after hot stamping process. J. Mater. Process. Technol. 212, 437 (2012).Google Scholar
Chen, W., Ackerson, P., and Molian, P.: CO2 laser welding of galvanized steel sheets using vent holes. Mater. Des. 30, 245 (2009).Google Scholar
Ribolla, A., Damoulis, G.L., and Batalha, G.F.: The use of Nd: YAG laser weld for large scale volume assembly of automotive body in white. J. Mater. Process. Technol. 164, 1120 (2005).Google Scholar
Xia, M., Sreenivasan, N., Lawson, S., Zhou, Y., and Tian, Z.A.: Comparative study of formability of diode laser welds in DP980 and HSLA steels. ASME Trans. 129, 446 (2009).Google Scholar
Wu, Q., Gong, J., Chen, G., and Xu, L.: Research on laser welding of vehicle body. Opt. Laser Technol. 40, 420 (2009).Google Scholar
Farabi, N., Chen, D.L., and Zhou, Y.: Microstructure and mechanical properties of laser welded dissimilar DP600/DP980 dual-phase steel joints. J. Alloys Compd. 509, 982 (2011).Google Scholar
Quinto, L., Costa, A., Miranda, R., Yapp, D., Kumar, V., and Kong, C.J.: Welding with high power fiber lasers–A preliminary study. Mater. Des. 28, 1231 (2007).Google Scholar
Chen, H.C., Pinkerton, A.J., Li, L., Liu, Z., and Mistry, A.T.: Gap-free fibre laser welding of Zn-coated steel on Al alloy for light-weight automotive applications. Mater. Des. 32, 495 (2011).Google Scholar
Cui, C.Y., Cui, X.G., Ren, X.D, Liu, T.T., Hu, J.D., and Wang, Y.M.: Microstructure and microhardness of fiber laser butt welded joint of stainless steel plates. Mater. Des. 49, 761 (2013).Google Scholar
Jia, J., Yang, S.L., Ni, W.Y., Bai, J.Y., and Ding, B.: Study on microstructure and properties of laser welding joints of marine high strength steel E36. Chin. J. Lasers 41, 0203002 (2014).Google Scholar
Xia, M.S., Biro, E., Tian, Z.L., and Zhou, Y.: Effects of heat input and martensite on HAZ softening in laser welding of dual phase steels. ISIJ Int. 48, 809 (2008).Google Scholar
Han, T.K., Park, B.G., and Kang, C.Y.: Hardening characteristics of CO2 laser welds in advanced high strength steel. Met. Mater. Int. 18, 473 (2012).Google Scholar
Turetta, A., Bruschi, S., and Ghiotti, A.: Investigation of 22MnB5 formability in hot stamping operations. J. Mater. Process. Technol. 177, 396 (2006).Google Scholar
Liu, M.Y., Shi, B., Wang, C., Ji, S.K., Cai, X., and Song, H.W.: Normal Hall-Petch behavior of mild steel with submicron grains. Mater. Lett. 5, 2798 (2003).Google Scholar
Grishunin, V.A., Gromov, V.E., Ivanov, Y.F., Volkov, K.V., and Konovalov, S.V.: Evolution of the phase composition and defect substructure in the surface layer of rail steel under fatigue. Steel Transl. 43, 724 (2013).CrossRefGoogle Scholar
Takeda, T., Shindo, Y., and Narita, F.: Vacuum crack growth behavior of austenitic stainless steel under fatigue loading. Strength Mater. 43, 532 (2011).Google Scholar