Solution Transformation of Metal Thin Films to II-VI Semiconductor Films

Published online by Cambridge University Press:  24 January 2012

Adam F. Gross*
Affiliation:
HRL Laboratories, LLC, 3011 Malibu Canyon Rd, Malibu, CA 90265
Get access

Abstract

The low temperature solution based transformation of silver metal layers to II-VI materials is investigated as an alternative mechanism for forming semiconductor thin films. This metal to semiconductor conversion has been demonstrated with the solution based sulfurization and ion exchange of silver nanoparticles, but not to our knowledge on thin films. Starting with metal films is attractive because they may be scalably deposited on many substrates through evaporation or electro- and electroless plating. The metal to II-VI transformation is challenging in films because diffusion occurs directionally and because the ∼40% increase in lattice expansion may cause debonding. Silver films were deposited on glass with Ti adhesion layers and successfully transformed to well-adhered CdS and MnS films at ≤ 60 ºC. The II-VI compounds were confirmed by XRD and shown to be polycrystalline with SEM. Electrical conductivities, bandgaps, and optical absorption spectra were measured. These results demonstrate that solution based sulfurization and ion-exchange is a viable mechanism for forming II-VI semiconductor thin films with good conductivities from metal films at low temperatures.

Type
Research Article
Copyright
Copyright © Materials Research Society 2012

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

REFERENCES

1. Trindade, T., O’Brien, P. and Pickett, N. L., Chem. Mater. 13, 3843 (2001).Google Scholar
2. Lincot, D., Thin Solid Films 487, 40 (2005).Google Scholar
3. Hodes, G., Phys. Chem. Chem. Phys. 9, 2181 (2007).Google Scholar
4. Perelaer, J., Smith, P. J., Mager, D., Soltman, D., Volkman, S. K., Subramanian, V., Korvink, J. G. and Schubert, U. S., J. Mater. Chem. 20, 8466 (2010).Google Scholar
5. Mitzi, D. B., Adv. Mater. 21, 3141 (2009).Google Scholar
6. Todorov, T. K., Reuter, K. B. and Mitzi, D. B., Adv. Mater. 22, E156 (2010).Google Scholar
7. Liang, Y. N., Lok, B. K. and Hu, X., Electronics Packaging Technology Conference, 2009. EPTC ’09. 11th 174 (2009).Google Scholar
8. Zhang, J., Tang, Y. and Ouyang, M., Science 327, 1634 (2010).Google Scholar
9. Jeong, U., Xia, Y. and Yin, Y., Chem. Phys. Lett. 416, 246 (2005).Google Scholar
10. Camargo, P. H. C., Lee, Y. H., Jeong, U., Zou, Z. and Xia, Y., Langmuir 23, 2985 (2007).Google Scholar
11. Zhu, W., Wang, W. and Shi, J., J. Phys. Chem. B 110, 9775 (2006).Google Scholar
12. Son, D. H., Hughes, S. M., Yin, Y. and Alivisatos, A. P., Science 306, 1009 (2004).Google Scholar
13. Kulkarni, A. B., Uplane, M. D. and Lokhande, C. D., Mater. Chem. Phys. 41, 75 (1995).Google Scholar
14. Wilson, T. M., Int. J. Quantum Chem. 4 S3b, 757 (1970).Google Scholar
15. Hayashi, T., Nishikura, T., Suzuki, T. and Ema, Y., J. Appl. Phys. 64, 3542 (1988).Google Scholar
16. Kasap, S., Koughia, C., Singh, J., Ruda, H. and O’Leary, S. K. in Springer Handbook of Electronic and Photonic Materials, edited by Kasap, S. and Capper, P., (Springer Science + Business Media, New York, 2006) pp. 5763.Google Scholar
17. Praminik, P., Akhter, M. A. and Basu, P. K., Thin Solid Films 158, 271 (1988).Google Scholar
18. Sebastian, P. J., App. Phys. Lett. 62, 2956 (2003).Google Scholar
19. Garcia-Cuenca, M. V. and Morenza, J. L., J. Phys. D: Appl. Phys. 18, 2081 (1985).Google Scholar
20. Dhanam, M., Kavitha, B., Priya, M. S., J. Ovonic Res. 6, 1 (2010).Google Scholar
21. Goss, C. A., Charych, D. H., Majda, M., Anal. Chem. 63, 85 (1991).Google Scholar