Thermal and Dielectric Stability of Parylene X

Published online by Cambridge University Press:  01 February 2011

Jay J. Senkevich
Affiliation:
jsenkevich@brewerscience.com, Brewer Science Inc., n/a, 2401 Brewer Drive, Rolla, MO, 65401, United States
Brad Carrow
Affiliation:
trapskeetman@hotmail.com, Brewer Science Inc., 2401 Brewer Drive, Rolla, MO, 65401, United States
Pei-I Wang
Affiliation:
wangp3@rpi.edu, Rensselaer Polytechnic Institute, Center for Integrated Electronics, 110 8th St., Troy, NY, 12180, United States
Get access

Abstract

Integrating pore sealing and barrier dielectric materials into back-end-of-the-line (BEOL) structures is challenging due to the requirements of high thermal stability, electrical stability (high breakdown, low leakage, and low dielectric constant), and barrier-like properties of the films. With Al etch-back metallization the dielectric needed to be stable to 450 °C due to Al reflow but now the thermal budget is shrinking with Cu metallization. Now the limiting factors are solder and ultra-low k (ULK) dielectric cure temperatures. These temperatures may still require thermal anneals exceeding 400 °C, which is very demanding on organic-based systems. Parylene X, a pore sealing chemical vapor depositable polymer, is deposited a room temperature via a precursor that allows the polymer to be self-initiated and without any by-products. The deposition platform allows controlled penetration of the organic polymer that allows significant fracture toughness improvement for the ULK dielectric. The polymer starts to cross-link at 175 °C with full conversion by 380 °C as measured by FT-IR spectroscopy. The polymer is shown to be stable to 420 °C with a dielectric constant of 2.7 and a leakage current of 0.5 × 10-9 A/cm2 at 0.67 MV/cm using MIMCAP structures. Parylene × was shown to have barrier-like properties in contact with both Ta and Cu metallization using bias-temperature stress (BTS) measurements at 0.5 MV/cm and 150 °C. In a Cu/Ta/parylene X/ULK dielectric stack, Ta a carbide former, can be used as an adhesive layer linking Cu to parylene × or the organic-based surface since parylene × has barrier-like properties.

Type
Research Article
Copyright
Copyright © Materials Research Society 2006

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

1 Yi, Z., Wen, Z., TzuFang, H., Nemani, S., Sub, Y. Kang, Amer, H., Li-Qun, X., and M'Saad, H., Adv. Metal. Conf. 21-23 Oct. 2003, Montreal, Que pp. 543–7 (2004).Google Scholar
2 Jain, S., Zubkov, V., Nowak, T., Demos, A., and Rocha, J., Solid State Technol. 48(9), 43–4 (2005).Google Scholar
3 Maindenberg, D.A., Volksen, W., Miller, R.D., and Dauskart, R.H., Nature Materials 3(7), 464–9 (2004).Google Scholar
4 Hoyas, A. Martin, Schuhmacher, J., Whelan, C.M., Celis, J.P., and Maex, K., Microelectron. Eng. 76(1-4), 32–7 (2004).Google Scholar
5 Jezewski, C., Lanford, W.A., Senkevich, J.J., Wiegand, C. J., Mallikarjunan, A., Lu, D., Wang, G.-C., Lu, T.-M., and Jin, C., J. Electrochem. Soc. 151(7), F157161 (2004).Google Scholar
6 Senkevich, J.J., Wiegand, C.J., Yang, G.-R., and Lu, T.-M., Chem. Vapor. Dep. 10(5) 247–9 (2004).Google Scholar
7 Bae, D.-L., Jezewski, C., Cale, T.S., and Senkevich, J.J., Chem. Vapor. Dep. 11(4), 191193 (2005).Google Scholar
8 Juneja, J.S., Eyck, G.A. Ten, Bakhru, H., and Lu, T.-M., J. Vac. Sci. Technol. B 23(5), 2232–5 (2005).Google Scholar
9 Senkevich, J.J., Mallikarjunan, A., Wiegand, C.J., Lu, T.-M., Bani-Salameh, H.N., and Lichti, R.L., Electrochem. Solid-State Lett. 7(4) G5658 (2004).Google Scholar
10 Carrow, B.P., Murray, R.E., Woods, B.W., and Senkevich, J.J. in Materials, Technology and Reliability of Advanced Interconnects edited by Besser, P.R., McKerrow, A.J., Iacopi, F., Wong, C.P., and Vlassak, J.J. (Mater. Res. Soc. Sympos. Proc. 863, Pittsburgh, PA, 2005) pp.189194.Google Scholar
11 Senkevich, J.J., Carrow, B.P., Woods, B.W., Bae, D.-L., Cale, T.S., and Wang, P.-I Adv. Metal. Conf. (AMC), September 27-29, 2005, Colorado Springs, Colorado. pp. 375–9 (2006).Google Scholar
12 Mallikarjunan, A., Yang, G., Senkevich, J. J., Wiegand, C., Williams, E., and Lu, T.-M., Electrochem. Solid-State Lett. 6(8), F28–F29 (2003).Google Scholar
13 Wang, P.-I., Wiegand, C. J., Senkevich, J.J., and Lu, T.-M., Appl. Phys. Lett. 84(14), 2617–19 (2004).Google Scholar
14 Juneja, J.S., Wang, P.-I., Karabacak, T., and Lu, T.-M., Thin Solid Films 504, 239242 (2006).Google Scholar
15 Gaynor, J., Chen, J., Nguyen, H., Brown, G., Taylor, K., Luttmer, J.D., Plano, M., Cleary, T., Wing, J., and Kelly, J. in low and high dielectric constant materials: materials science processing and reliability issues (Proc. Electrochem. Soc. 97–8 1997) pp. 157–67.Google Scholar
16 Senkevich, J.J., J. Vac. Sci. & Tech. A 18(5), 2586–90 (2000).Google Scholar
17 Senkevich, J.J., Carrow, B.P., Woods, B.W., and Murray, R.E., The Twenty Second International VLSI/ULSI Multilevel Interconnection Conference (2005 VMIC), October 3 – 6, 2005, Fremont, CA, pp. 468–73.Google Scholar
18 Senkevich, J.J., Mitchell, C.J., Vijayaraghavan, A., Barnat, E.V., McDonald, J.F., and Lu, T.-M., J. Vac. Sci. & Tech. A 20(4), 1445–9 (2002).Google Scholar