Influence of the microstructure of Pt/Si substrates on textured growth of barium titanate thin films prepared by pulsed laser deposition

Published online by Cambridge University Press:  31 January 2011

Cheol Seong Hwang ,
Mark D. Vaudin  and
Peter K. Schenck
Cheol Seong Hwang
Affiliation:
National Institute of Standards and Technology, Gaithersburg, Maryland 20899
Mark D. Vaudin
Affiliation:
National Institute of Standards and Technology, Gaithersburg, Maryland 20899
Peter K. Schenck
Affiliation:
National Institute of Standards and Technology, Gaithersburg, Maryland 20899
Get access

Extract

Pt-coated silicon substrates with strong (111) Pt texture were annealed in an oxidizing atmosphere at temperatures from 500 °C to 750 °C. BaTiO3 thin films were deposited by pulsed laser ablation on the substrates. Observation by transmission electron microscopy showed that the substrate anneal caused the formation of TiO2 in the Pt layer, accompanied by the formation of a high density of faceted protrusions on the Pt surface, particularly at the higher anneal temperatures. The Pt protrusions had (111) facets, parallel to the substrate surface, on which (100)-oriented BaTiO3 grains were observed. BaTiO3 grains with an epitaxial relationship to the Pt lattice were observed on inclined facets of the Pt protrusions [which were not (111) planes], and also on the nonplanar regions of the Pt surface. These epitaxial BaTiO3 grains had (111) preferred orientation relative to the substrate surface. Thus, the BaTiO3 films displayed bimodal growth behavior, with both (100) texture and (111) epitaxy. We propose a model for this behavior based on surface energy considerations.

Type
Articles
Information
Journal of Materials Research , Volume 13 , Issue 2 , February 1998 , pp. 368 - 375
Copyright
Copyright © Materials Research Society 1998

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

REFERENCES

1. For example, Ferroelectric Thin Films, edited by Myers, E.R. and Kingon, A. I. (Mater. Res. Soc. Symp. Proc. 200, Pittsburgh, PA, 1990);Google Scholar
Ferroelectric Thin Films II, edited by Kingon, A. I., Myers, E.R., and Tuttle, B. (Mater. Res. Soc. Symp. Proc. 243, Pittsburgh, PA, 1992);Google Scholar
Ferroelectric Thin Films III, edited by Tuttle, B.A., Myers, E.R., Desu, S. B., and Larsen, P.K. (Mater. Res. Soc. Symp. Proc. 310, Pittsburgh, PA, 1993).Google Scholar
2.Parker, L.H. and Tasch, A. F., IEEE Circuits Dev. Mag. 6, 17 (1990).CrossRefGoogle Scholar
3.Auciello, O. and Kingon, A. I., in Proc. of the 8th Int. Symp. on Applications of Ferroelectrics, edited by Liu, M. (IEEE, 1992), p. 320.Google Scholar
4.Hsu, S. T. and Kalish, I.H., Integr. Ferroelec. 2, 179 (1992).CrossRefGoogle Scholar
5.Ramesh, R., Sands, T., Keramidas, V.G., and Fork, D.K., in Ferroelectric Thin Films III, edited by Tuttle, B.A., Myers, E.R., Desu, S.B., and Larsen, P.K. (Mater. Res. Soc. Symp. Proc. 310, Pittsburgh, PA, 1993), pp. 195–200.Google Scholar
6.Kwok, C.K., Vijay, D. P., Desu, S.B., Parikh, N.R., and Hill, E.A., Integr. Ferroelec. 3, 121 (1993).CrossRefGoogle Scholar
7.Hren, P.D., Rou, S.H., Al-Shareef, H.N., Ameen, M. S., Au-ciello, O., and Kingon, A. I., Integr. Ferroelec. 2, 311 (1992).CrossRefGoogle Scholar
8.Waser, R. and Klee, M., Integr. Ferroelec. 2, 23 (1992).CrossRefGoogle Scholar
9.Scott, J. F., Melnick, B.M., Mcmillan, L.D., and Paz de Araujo, C.A., Integr. Ferroelec. 3, 225 (1993).Google Scholar
10.Bruchhaus, R., Pitzer, D., Eibl, O., Scheithauer, U., and Hoesler, W., in Ferroelectric Thin Films II, edited by Kingon, A. I., Myers, E.R., and Tuttle, B.A. (Mater. Res. Soc. Symp. Proc. 243, Pittsburgh, PA, 1992), pp. 123–128.Google Scholar
11.Olowolafe, J.O., Jones, R. E., Campbell, A. C., Maniar, P.D., Hedge, R. I. and Mogab, C. J., in Ferroelectric Thin Films II, edited by Kingon, A. I., Myers, E.R., and Tuttle, B.A. (Mater. Res. Soc. Symp. Proc. 243, Pittsburgh, PA, 1992), pp. 355–360.Google Scholar
12.Powder Diffraction File, International Center for Diffraction Data, Newtown Square, PA, 1996.Google Scholar
13.Spierings, G.A.C.M., Van Zon, J.B.A., and Larsen, P.K., Integr. Ferroelec. 3, 283 (1993).Google Scholar
14.Gaskell, D.R., Introduction to Metallurgical Thermodynamics (McGraw-Hill Book Company, New York, 1973), p. 498.Google Scholar
15.Deal, B. E. and Grove, A. S., J. Appl. Phys. 36, 3770 (1965).Google Scholar
16.Tani, T., Xu, Z., and Payne, D.A., in Ferroelectric Thin Films III, edited by Tuttle, B.A., Myers, E.R., Desu, S. B., and Larsen, P.K. (Mater. Res. Soc. Symp. Proc. 310, Pittsburgh, PA, 1993), pp. 269–274.Google Scholar