Physical Metallurgy and Properties of β-solidifying TiAl Based Alloys

Published online by Cambridge University Press:  18 January 2011

Helmut Clemens ,
Thomas Schmoelzer ,
Martin Schloffer ,
Emanuel Schwaighofer ,
Svea Mayer  and
Gerhard Dehm
Helmut Clemens
Affiliation:
Department of Physical Metallurgy and Materials Testing, Montanuniversität Leoben, A-8700, Leoben, Austria
Thomas Schmoelzer
Affiliation:
Department of Physical Metallurgy and Materials Testing, Montanuniversität Leoben, A-8700, Leoben, Austria
Martin Schloffer
Affiliation:
Department of Physical Metallurgy and Materials Testing, Montanuniversität Leoben, A-8700, Leoben, Austria
Emanuel Schwaighofer
Affiliation:
Department of Physical Metallurgy and Materials Testing, Montanuniversität Leoben, A-8700, Leoben, Austria
Svea Mayer
Affiliation:
Department of Physical Metallurgy and Materials Testing, Montanuniversität Leoben, A-8700, Leoben, Austria
Gerhard Dehm
Affiliation:
Department of Materials Physics, Montanuniversität Leoben, A-8700, Leoben, Austria
Get access

Abstract

In this paper, the physical metallurgy and properties of a novel family of high-strength γ-TiAl-based alloys is reviewed succinctly. These so-called TNM™ alloys contain Nb and Mo additions in the range of 3 - 7 atomic percent as well as small additions of B and C. For the definition of the alloy composition thermodynamic calculations using the CALPHAD method were conducted. The predicted phase transformation and ordering temperatures were verified by differential scanning calorimetry and in situ high-energy X-ray diffraction. TNM alloys solidify via the β-phase and exhibit an adjustable β-phase volume fraction at temperatures, where hot-working processes are performed. Due to the high volume fraction of β-phase these alloys can be processed isothermally as well as under near conventional conditions. In order to study the occurring deformation and recrystallization processes during hot-working, in situ diffraction experiments were conducted during compression tests at elevated temperatures. With subsequent heat-treatments a significant reduction of the β-phase is achieved. These outstanding features of TNM alloys distinguish them from other TiAl alloys which must exclusively be processed under isothermal conditions and/or which always exhibit a high fraction of β-phase at service temperature. After hot-working and multi-step heat-treatments, these alloys show yield strength levels > 800 MPa at room temperature and also good creep resistance at elevated temperatures.

Keywords

ductilityphase transformationmicrostructure
Type
Research Article
Information
MRS Online Proceedings Library (OPL) , Volume 1295: Symposium N – Intermetallic-Based Alloys for Structural and Functional Applications , 2011 , mrsf10-1295-n03-03
Copyright
Copyright © Materials Research Society 2011

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

REFERENCES

1. Structural Aluminides for Elevated Temperatures, edited by Kim, Y-W., Morris, D., Yang, R., and Leyens, C. (TMS, Warrendale PA, 2008).Google Scholar
2. Tetsui, T.: in Gamma Titanium Aluminides 1999, edited by Kim, Y-W., Dimiduk, D. M. and Loretto, M. H., TMS, Warrendale, PA, USA (1999), p. 15.Google Scholar
3. Bewlay, B. P.: Presentation at the European Symposium on Superalloys and their Applications, Wildbad Kreuth, Germany (May 25-28, 2010).Google Scholar
4. Clemens, H. et al. , Intermetallics 16, 827 (2008).Google Scholar
5. Clemens, H. et al. , Adv. Eng. Mater. 10, 707 (2008).Google Scholar
6. Küstner, V. et al. , in Gamma Titanium Aluminides 2003, edited by Kim, Y-W., Clemens, H. and Rosenberger, A. H. (Warrendale, PA: TMS, 2003), p. 89.Google Scholar
7. Wallgram, W. et al. , Int. J. Mat. Res. 100, 1021 (2009).Google Scholar
8. Saunders, N., in Gamma Titanium Aluminides 1999, edited by Kim, Y-W., Dimiduk, D.M. and Loretto, M.H. (TMS, Warrendale PA, 1999), p. 183.Google Scholar
9. Appel, F., Oehring, M., Wagner, R., Intermetallics 8, 1283 (2000).Google Scholar
10. Kainuma, R., Fujita, Y., Mitsui, H., Ohnuma, I., Ishida, K.: Intermetallics 8, 855 (2000).Google Scholar
11. Hecht, U. et al. : Intermetallics 18, 969 (2008).Google Scholar
12. Clemens, H. et al. , Mater. Res. Soc. Symp. Vol. 1128, 1128-U03-06 (2009).Google Scholar
13. Schmoelzer, T. et al. , Intermetallics 18, 1544 2010).Google Scholar
14. Watson, I. J. et al. , Adv. Eng. Mater. 11, 932 (2009).Google Scholar
15. Rizzi, N.: Presentation at the Symposium “Structural Aluminides for Elevated Temperature Applications”, TMS 2008 Annual Meeting, New Orleans, LA, USA (March 9-13, 2008).Google Scholar
16. Liss, K.-D. et al. , J. Appl. Phys. 106, 113536 (2009).Google Scholar
17. Schloffer, M., Diploma thesis, Montanuniversität, Leoben, Austria (2010).Google Scholar
18. Cha, L. et al. , Adv. Mater. Res. Vols. 146-147, 1365 (2011).Google Scholar
19. Schmoelzer, T. et al. : Adv. Eng. Mater (2011), in print.Google Scholar
20. Clemens, H., Kestler, H., Adv. Eng. Mater. 2, 551 (2000).Google Scholar