Quantitative Analyses of Precession Diffraction Data for a Large Cell Oxide

Christopher S.  Own  a1 c1 , Arun K.  Subramanian  a1 and Laurence D.  Marks  a1
a1 Department of Materials Science, Northwestern University, 2220 N. Campus Dr., Cook 2036, Evanston, IL 60201, USA

Article author query
own cs   [PubMed][Google Scholar] 
subramanian ak   [PubMed][Google Scholar] 
marks ld   [PubMed][Google Scholar] 

Abstract

Kinematical and two-beam calculations have been conducted and are compared to experimental precession data for the large unit cell crystal La4Cu3MoO12. Precession electron diffraction intensities are found to exhibit approximate two-beam behavior and demonstrate clear advantages over conventional SADP intensities for use in structure solution.

(Received January 30 2003)
(Accepted May 28 2003)


Key Words: TEM; electron; precession; diffraction; direct methods.