Direct foaming and seeding of highly porous, lightweight gypsum

Published online by Cambridge University Press:  15 July 2016

Elisabet Roch Isern  and
Gary L. Messing
Elisabet Roch Isern*
Affiliation:
Department of Materials Science and Engineering, Pennsylvania State University, University Park, PA16802
Gary L. Messing
Affiliation:
Department of Materials Science and Engineering, Pennsylvania State University, University Park, PA16802
*
a)Address all correspondence to this author. e-mail: eroch.isern@gmail.com
Get access

Abstract

This paper describes the direct-foaming of plaster of Paris (CaSO4·½H2O) with up to 1.7 wt% of a nonionic surface-active agent to obtain highly porous, lightweight gypsum (CaSO4·2H2O) with 65–70% total porosity and a homogeneous, bimodal pore size distribution. Based on viscosity and temperature changes in the setting plaster of Paris slurry, the nonionic surfactant is seen to retard gypsum crystallization and thus extend the working time at higher water to solid ratios. The increase in viscosity during gypsum crystallization stabilizes the macropores formed during foaming. Gypsum foams of 32% density with a submicron matrix pore size, and relatively uniform macropore size of ∼100 µm were obtained. Seeding the process with 0.5 wt% 100 µm diameter gypsum particles accelerates gypsum crystallization in the presence of the nonionic surfactant and results in a more uniform, finer (92 µm) macropore structure due to less time for bubble coalescence.

Keywords

insulatorfoamporosity
Type
Articles
Information
Journal of Materials Research , Volume 31 , Issue 15 , 15 August 2016 , pp. 2244 - 2251
Check for updates
Copyright
Copyright © Materials Research Society 2016 

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

REFERENCES

Gypsum Mineral Data. Available at: http://webmineral.com/data/Gypsum.shtml#.VErl9L4tZEQ (accessed February 23, 2016).Google Scholar
Yu, Q.L. and Brouwers, H.J.H.: Thermal properties and microstructure of gypsum board and its dehydration products: A theoretical and experimental investigation. Fire Mater. 36(7), 575 (2011).Google Scholar
Mahmoud, M.H.H., Rashad, M.M., Ibrahim, I.A., and Abdel-Aal, E.A.: Crystal modification of calcium sulfate dehydrate in the presence of some surface-active agents. J. Colloid Interface Sci. 270, 99 (2003).Google Scholar
Vekinis, G., Ashby, M.F., and Beaumont, P.W.R.: Plaster of Paris as a model material for brittle porous solids. J. Mater. Sci. 28, 3221 (1993).Google Scholar
Studart, A.R., Gonzenbach, U.T., Tervoort, E., and Gauckler, L.J.: Processing routes to macroporous ceramics: A review. J. Am. Ceram. Soc. 89(6), 1771 (2006).Google Scholar
Hiemenz, P.C. and Rayagopalan, R.: Principles of Colloid and Surface Chemistry (Marcel Dekker, New York, 1997).Google Scholar
Pugh, R.J.: Handbook of Applied Surface and Colloid Chemistry, Vol. 2, , K. Holmberg, eds.; John Wiley & Sons Ltd.: West Sussex, 2003.Google Scholar
Singh, N.B. and Middendorf, B.: Calcium sulphate hemihydrate hydration leading to gypsum crystallization. Prog. Cryst. Growth Charact. Mater. 53, 57 (2007).CrossRefGoogle Scholar
Çolak, A.: Density and strength characteristics of foamed gypsum. Cem. Concr. Compos. 22, 193 (2000).Google Scholar
ASTM International D 1200-10: Standard Test Method for Viscosity by Ford Viscosity Cup (ASTM International, West Conshohocken, PA, 2005).Google Scholar
Patton, T.C.: Paint Flow, and Pigment Dispersion (John Wiley & Sons Ltd, New York, 1979).Google Scholar
ASTM Standard E112-96: Standard Test Methods for Determining Average Grain Size (ASTM International, West Conshohocken, PA, 2004).Google Scholar