Interfacial reactions and shear strength on Cu and electrolytic Au/Ni metallization with Sn-Zn solder

Published online by Cambridge University Press:  01 June 2006

Jeong-Won Yoon  and
Seung-Boo Jung
Jeong-Won Yoon
Affiliation:
School of Advanced Materials Science and Engineering, Sungkyunkwan University, Jangan-gu, Suwon, Gyeonggi-do 440-746, Korea
Seung-Boo Jung*
Affiliation:
School of Advanced Materials Science and Engineering, Sungkyunkwan University, Jangan-gu, Suwon, Gyeonggi-do 440-746, Korea
*
a) Address all correspondence to this author. e-mail: sbjung@skku.ac.kr
Get access

Abstract

The interfacial reaction between eutectic Sn-9 wt% Zn solder and two different kinds of ball-grid-array substrates (Cu and Au/Ni electroplated Cu) during aging at 150 °C and the shear strength of the resulting joints were investigated. In the Sn-9Zn/Cu joints, only Cu5Zn8 intermetallic compound (IMC) was observed between the solder and Cu layer during the first 100 h of aging. After aging for 1000 h, the layer-type Cu5Zn8 IMC layer was disrupted at the interface, causing it to act as a channel for the diffusion of Sn. As a result, Cu6Sn5 and Cu3Sn IMCs were formed underneath the Cu5Zn8 IMC layer. This interfacial reaction significantly degraded the joint strength. In the case of the Au/Ni/Cu substrate, an AuZn3 IMC layer formed at the interface because of the fast reaction between Au and Zn. In addition, the AuZn3 IMC layer became detached from the interface during reflow. The detachment of the AuZn3 IMC layer is presumably from the mismatch in the coefficients of thermal expansion and weak adhesion between the AuZn3 IMC layer and Ni layer caused by the depletion of the Au layer. When the aging time was extended to 100 h, Ni5Zn21 IMC was observed on the Ni substrate. The shear strength of the aged Sn-9Zn/Au/Ni/Cu joint was significantly related to the detachment of the AuZn3 IMC layer. After aging at 150 °C, fracturing occurred on the detached AuZn3 IMC layer. To ensure the reliability of the Sn-Zn/Au/Ni/Cu joint, the detachment of the AuZn3 IMC needs to be prevented.

Keywords

Electronic materialMicroelectronicsPackaging
Type
Articles
Information
Journal of Materials Research , Volume 21 , Issue 6 , June 2006 , pp. 1590 - 1599
Copyright
Copyright © Materials Research Society 2006

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

REFERENCES

1.Abtew, M., Selvaduray, G.: Lead-free solders in microelectronics. Mater. Sci. Eng. R R27, 95 (2000).CrossRefGoogle Scholar
2.Zeng, K., Tu, K.N.: Six cases of reliability study of Pb-free solder joints in electronic packaging technology. Mater. Sci. Eng. R 38, 55 (2002).CrossRefGoogle Scholar
3.Islam, M.N., Chan, Y.C., Sharif, A.: Interfacial reactions of Sn-Cu and Sn-Pb-Ag solder with Au/Ni during extended time reflow in ball grid array packages. J. Mater. Res. 19, 2897 (2004).CrossRefGoogle Scholar
4.Liu, Y.H., Chuang, C.M., Lin, K.L.: Failure behavior upon shear test of 5Sn-95Pb solder bump after high temperature reliability test. J. Mater. Res. 19, 2471 (2004).CrossRefGoogle Scholar
5.Alam, M.O., Chan, Y.C., Tu, K.N.: Effect of reaction time and P content on mechanical strength of the interface formed between eutectic Sn-Ag solder and Au/electroless Ni(P)/Cu bond pad. J. Appl. Phys. 94, 4108 (2003).CrossRefGoogle Scholar
6.Chen, W.T., Ho, C.E., Kao, C.R.: Effect of Cu concentration on the interfacial reactions between Ni and Sn-Cu solders. J. Mater. Res. 17, 263 (2002).CrossRefGoogle Scholar
7.Yoon, J.W., Kim, S.W., Koo, J.M., Kim, D.G., Jung, S.B.: Reliability investigation and interfacial reaction of ball-grid-array packages using the lead-free Sn-Cu solder. J. Electron Mater. 33, 1190 (2004).CrossRefGoogle Scholar
8.Hwang, C.W., Suganuma, K., Kiso, M., Hashimoto, S.: Interface microstructures between Ni-P alloy plating and Sn-Ag-(Cu) lead-free solders. J. Mater. Res. 18, 2540 (2003).CrossRefGoogle Scholar
9.Sohn, Y.C., Yu, J., Kang, S.K., Shih, D.Y., Lee, T.Y.: Spalling of intermetallic compounds during the reaction between lead-free solders and electroless Ni-P metallization. J. Mater. Res. 19, 2428 (2004).CrossRefGoogle Scholar
10.Chen, Z., He, M., Qi, G.: Morphology and kinetic study of the interfacial reaction between the Sn-3.5Ag solder and electroless Ni-P metallization. J. Electron Mater. 33, 1465 (2004).CrossRefGoogle Scholar
11.Tu, K.N., Gusak, A.M., Li, M.: Physics and materials challenges for lead-free solders. J. Appl. Phys. 93, 1335 (2003).CrossRefGoogle Scholar
12.Yoon, J.W., Lee, C.B., Jung, S.B.: Growth of an intermetallic compound layer with Sn-3.5Ag-5Bi on Cu and Ni-P/Cu during aging treatment. J. Electron Mater. 32, 1195 (2003).CrossRefGoogle Scholar
13.Jang, J.W., Frear, D.R., Lee, T.Y., Tu, K.N.: Morphology of interfacial reaction between lead-free solders and electroless Ni-P under bump metallization. J. Appl. Phys. 88, 6359 (2000).CrossRefGoogle Scholar
14.Suganuma, K., Murata, T., Noguchi, H., Toyoda, Y.: Heat resistance of Sn-9Zn solder/Cu interface with or without coating. J. Mater. Res. 15, 884 (2000).CrossRefGoogle Scholar
15.Kim, K.S., Ryu, K.W., Yu, C.H., Kim, J.M.: The formation and growth of intermetallic compounds and shear strength at Sn-Zn solder/Au-Ni-Cu interfaces. Microelectron Reliab. 45, 647 (2005).CrossRefGoogle Scholar
16.Date, M., Tu, K.N., Shoji, T., Fujiyoshi, M., Sato, K.: Interfacial reactions and impact reliability of Sn-Zn solder joints on Cu or electroless Au/Ni(P) bond-pads. J. Mater. Res. 19, 2887 (2004).CrossRefGoogle Scholar
17.Sogo, Y., Hojo, T., Iwanishi, H., Hirose, A., Kobayashi, K.F., Yamaguch, A., Furusawa, A., Nishida, K.: Influence of the interfacial reaction layer on reliability of CSP joints using Sn-8Zn-3Bi solder and Ni/Au plating. Mater. Trans. 45, 734 (2004).CrossRefGoogle Scholar
18.Huang, C.W., Lin, K.L.: Interfacial reactions of lead-free Sn-Zn based solders on Cu and Cu plated electroless Ni-P/Au layer under aging at 150 °C. J. Mater. Res. 19, 3560 (2004).CrossRefGoogle Scholar
19.Vaynman, S., Ghosh, G., Fine, M.E.: Some fundamental issues in the use of Zn-containing lead-free solders for electronic packaging. Mater. Trans. 45, 630 (2004).CrossRefGoogle Scholar
20.Hirose, A., Yanagawa, H., Ide, E., Kobayashi, K.F.: Joint strength and interfacial microstructure between Sn-Ag-Cu and Sn-Zn-Bi solders and Cu substrate. Sci. Technol. Adv. Mater. 5, 267 (2004).CrossRefGoogle Scholar
21.Yu, S.P., Hon, M.H., Wang, M.C.: The adhesion strength of a lead-free solder hot-dipped on copper substrate. J. Electron Mater. 29, 237 (2000).CrossRefGoogle Scholar
22.Lee, C.B., Jung, S.B., Shin, Y.E., Shur, C.C.: Effect of isothermal aging on ball shear strength in BGA joints with Sn-3.5Ag-0.75Cu solder. Mater. Trans. 43, 1858 (2002).CrossRefGoogle Scholar
23.Hwang, C.W., Kim, K.S., Suganuma, K.: Interfaces in lead-free soldering. J. Electron Mater. 32, 1249 (2003).CrossRefGoogle Scholar
24.Massalski, T.B.: Binary Alloy Phase Diagrams 2nd ed. (ASM, New York, NY, 1987), p. 2887.Google Scholar
25.Yoon, J.W., Chun, H.S., Jung, S.B.: Interfacial reaction and mechanical characterization of eutectic Sn-Zn/ENIG solder joints during reflow and aging. Mater. Trans. 46, 2386 (2005).CrossRefGoogle Scholar