Synthesis and characterization of sol-gel derived hexa-aluminate phosphors

Published online by Cambridge University Press:  31 January 2011

D. Ravichandran
Affiliation:
Materials Research Laboratory, The Pennsylvania State University, University Park, Pennsylvania 16802
R. Roy
Affiliation:
Materials Research Laboratory, The Pennsylvania State University, University Park, Pennsylvania 16802
W. B. White
Affiliation:
Materials Research Laboratory, The Pennsylvania State University, University Park, Pennsylvania 16802
S. Erdei
Affiliation:
Materials Research Laboratory, The Pennsylvania State University, University Park, Pennsylvania 16802
Get access

Abstract

Two refractory phosphors, BaMg2Al16O27: Eu2+ (BAM) and MgAl11O17.5: Ce3+, Tb3+ (MAO), have been synthesized both by the conventional solid-state processing route (using oxides as the starting materials) and by reacting precursors made by the sol-gel process using organic precursors. The phases formed were reacted at 1000 °C in (a) steam and (b) steam + AlF3. The phosphors were well crystallized with particle sizes in the range of 1–10 μm. The emission spectra showed the characteristic broad band blue emission of Eu2+ for BAM and a narrow band green luminescence of Tb3+ for MAO. The melting points of BAM and MAO were measured to be 1920 ± 20 °C and 1950 ± 20 °C, respectively, using an Ir-strip furnace and optical pyrometer. BAM and MAO phosphor materials are congruently and incongruently melting, respectively. Excellent crystallization via the sol-gel route was found even at 1220 °C. Enhancement of the luminescent output by the steam treatment by some 25% was determined.

Type
Articles
Copyright
Copyright © Materials Research Society 1997

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

1.Stevels, A. L. N., J. Lumin. 17, 121 (1978).CrossRefGoogle Scholar
2.Verstegen, J. M. P. J. and Stevels, A. L. N., J. Lumin. 9, 406 (1974).CrossRefGoogle Scholar
3.Sommerdijk, J. L. and Verstegen, J. M. P. J., J. Lumin. 9, 415 (1974).CrossRefGoogle Scholar
4.Smets, B. M. J., Mater. Chem. Phys. 16, 283 (1987).CrossRefGoogle Scholar
5.Dutta, A. and Dullea, L. V., U.S. Patent No. 5, 160, 663, Nov. 3, 1992.Google Scholar
6.Bergstein, A. and White, W. B., J. Electrochem. Soc. 118, 1166 (1971).CrossRefGoogle Scholar
7.deJayer-Veenis, A. W. and Bril, A., J. Electrochem. Soc. 123, 1253 (1976).CrossRefGoogle Scholar
8.Verstegen, J. M. P. J., J. Solid State Chem. 7, 468 (1973).CrossRefGoogle Scholar
9.Bykovskii, P. I., Benderskaya, L. P., and Chernaya, N. G., Izv. Akad. Nauk SSSR, Neorg. Mater. 22, 1405 (1986).Google Scholar
10.Ronda, C. R. and Smets, B. M. J., J. Electrochem. Soc. 136, 570 (1989).CrossRefGoogle Scholar
11.Gobbels, M., Woermann, E., and Jung, J., J. Solid State Chem. 120, 358 (1995).CrossRefGoogle Scholar
12.Iyi, N., Gobbels, M., and Matsui, Y., J. Solid State Chem. 120, 364 (1995).CrossRefGoogle Scholar
13.Roy, R., Ravichandran, D., and White, W. B., J. Soc. Inform. Display 4, 183 (1996).CrossRefGoogle Scholar
14.Stevels, A. L. N. and Schrama-DePauw, A. D. M., J. Lumin. 14, 147 (1976).Google Scholar
15.Khan, A., Lejus, A. M., Madsac, M., Thery, J., Vivien, D., and Bernier, J. C., J. Appl. Phys. 52, 6864 (1981).CrossRefGoogle Scholar
16.Saber, D. and Lejus, A. M., Mater. Res. Bull. 16, 1365 (1981).CrossRefGoogle Scholar
17.Shafer, M. W. and Roy, R., J. Am. Ceram. Soc. 42, 563 (1959).CrossRefGoogle Scholar
18.Roy, R., Ravichandran, D., and White, W. B., Proc. of the 1st Int. Conf. on the Science and Tech. of Display Phosphors, pp. 197200, San Diego, CA, Nov. 14–16, 1995.Google Scholar